Why, yes. That MSH is not as dark as the rest. That's because the nickel-tungsten didn't plate as quickly, leaving a different composition at the surface. YAY!
So, I needs to do a Wood's strike on it, and try again.
Why, yes. That MSH is not as dark as the rest. That's because the nickel-tungsten didn't plate as quickly, leaving a different composition at the surface. YAY!
So, I needs to do a Wood's strike on it, and try again.
Is that the Burton gun?
May I ask what your doing? A PVD type process?
Regards,
Shane